7 Mar The ASTM D standard test method is recommended for the unidentified samples, as well as for samples where the fusion of the inorganic. This test method covers the determination of the ignition loss of cured reinforced resins by jose4diaz ASTM-D – Free download as PDF File .pdf), Text File .txt) or read online for free.
|Genre:||Health and Food|
|Published (Last):||18 February 2014|
|PDF File Size:||2.34 Mb|
|ePub File Size:||16.76 Mb|
|Price:||Free* [*Free Regsitration Required]|
Link to Active This astm d2584 will always route to the current Active version of the standard. It is the responsibility of whoever uses this standard to consult and establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
The ASTM D standard test method is recommended for the unidentified samples, as well as for samples where the astm d2584 of the inorganic portions is an issue. Astm d2584 Item s – proposed revisions of this standard. Historical Version s – xstm previous versions of standard.
Ignition Loss of Cured Reinforced Resins (ASTM D2584)
astm d2584 The test method determines the ignition loss of a cured reinforced resin sample and examines astm d2584 fiber architecture of pultruded structural shapes.
The procedure determines the residual solids in the polymer, however it cannot be used to locate the individual chemical components of ash.
These procedures do not include fluorinated polymers and polymers containing astm d2584 components. Procedure A is a muffle furnace technique d5284 samples up to 5 to 50 grams. Sign in Astm d2584 started. Adequate safeguards for personnel and property shall be employed in conducting these tests. Procedure B is a Rapid-Ash muffle furnace technique for samples up to 2 to 10 grams.
This test method astm d2584 not provide a measure of resin content for samples containing reinforcing materials that lose weight under the conditions of the test astm d2584 containing resins or fillers that do not decompose to volatile materials released by ignition.
Referenced Documents purchase separately The documents listed below are 2d584 within the subject standard but are not provided as part of the standard. The test method determines the inorganic content of plastics through the destructive ashing process. This ignition loss can be considered to be the resin content within the limitations of 4.
There are two procedures to determine the organic residue in plastic. astm d2584
These samples are flamed over a burner before being ashed in a furnace. The ASTM test method is recommended for evaluating the inorganic residues from plastics ash, which is important to study astm d2584 the atm process.
This test method can also be used to examine astm d2584 fiber architecture of pultruded structural shapes. The test method includes ash level of 0.
Never miss a story from Presto Groupwhen you sign up for Medium. If organic resin reinforcement is only glass fabric or filament wstm is dd2584 decomposed to volatile astm d2584 under the test conditions and the small amount of volatiles water, astm d2584 solvent are ignored, the resin content of the sample is considered as the ignition loss. Note 1—There is no known ISO equivalent to this standard. These samples are ignited and ashed in a furnace.
ASTM D – 11 Standard Test Method for Ignition Loss of Cured Reinforced Resins
The test methods do not measure the resin content of a sample that contains the reinforcing materials losing weight under test conditions or that contains resins or fillers that do not decompose to explosive materials released by ignition. Blocked Unblock Follow Astm d2584 updates. If only glass fabric or filament is used as the reinforcement of d22584 organic resin that is completely decomposed to volatile materials under the conditions astm d2584 this test and the small amount of volatiles water, residual solvent that are potentially present are ignored, the ignition loss can be astm d2584 to be the resin content of the sample.
This test method can be used astm d2584 obtain the ignition loss of a cured reinforced resin sample.